| 产品信息： |
|
性能项目 |
试验条件[状态] |
测试方法 |
数据单位 |
测试数据 |
|
LI-912 |
LI-941 |
|
物理性能 |
比重 |
23℃ |
ASTM D-792 |
g/cm3 |
1.07 |
1.07 |
|
熔体流动速率 |
220℃ 10kg |
ASTM D-1238 |
g/10min |
1.2 |
0.5 |
|
模塑收缩率 |
|
ASTM D-955 |
% |
0.4-0.7 |
0.4-0.7 |
|
机械性能 |
拉伸强度 |
50mm/min |
ASTM D-638 |
kg/cm2 |
480 |
480 |
|
屈服伸长率 |
50mm/min |
ASTM D-638 |
% |
6 |
6 |
|
断裂伸长率 |
50mm/min |
ASTM D-638 |
% |
25 |
25 |
|
弯曲强度 |
5mm/min |
ASTM D-790 |
kg/cm2 |
770 |
770 |
|
弯曲模量 |
5mm/min |
ASTM D-790 |
kg/cm2 |
22500 |
23500 |
|
IZOD冲击强度 |
1/4〃 Notched |
ASTM D-256 |
kg.cm/cm |
16 |
14 |
|
热性能 |
维卡软化点 |
5kg 50℃/nr |
ASTM-D1525 |
℃ |
95 |
104 |
|
热变形温度 |
18.6kg/cm2
unannealed) |
ASTM D-259 |
℃ |
97 |
105 |
|
1/4″,4.6kg/
(unannealed) |
ASTM D-259 |
℃ |
101 |
107 |
|
燃烧性 |
1/8″ |
UL-94 |
|
HB 黄卡链接 |
HB 黄卡链接 |
|
1/16″ |
|
HB |
HB |
|
特性 |
|
|
|
|
标准 |
超高耐热 |
|
|